Recording medium having high melting point recording layer, information recording method thereof, and information reproducing apparatus and method therefor

ABSTRACT

A simple-structured recording medium without a mask layer and information recording and reproducing methods, which resolve thermal stability related problems arising during reproduction, the recording medium including a high melting point recording layer between first and second dielectric layers. The method of recording information on the recording medium involves irradiating a laser beam onto the recording medium to induce reaction and diffusion in the high melting point recording layer and the first and second dielectric layers. The method of reproducing information recorded on such a super-resolution near-field recording medium by the above method involves generating plasmon using crystalline particles of the high melting point recording layer and the first and second dielectric layers as a scatter source to reproduce information regardless of a diffraction limit of a laser used.

CROSS-REFERENCE TO RELATED APPLICATIONS

This application is a National Stage of PCT Application No. PCT/KR2003/968, filed May 16, 2003 in the World Intellectual Property Office, and Japanese Patent Application No. 2002-141664 filed on May 16, 2002 in the Japanese Patent Office, the disclosures of which are incorporated herein by reference.

BACKGROUND OF THE INVENTION

1. Field of the Invention

The present invention relates to a recording medium, and more particularly, to a recording medium having a high melting point recording layer, an information recording method thereof, and an apparatus and method for reproducing information therefrom.

2. Description of the Related Art

Conventional recording media can be classified into magneto-optical recording media or phase change recording media. In magneto-optical recording media, such as mini disks (MDs), information is read by detecting the rotation of a straight polarized light reflected from a magnetic film depending on the magnetic force and the magnetization direction of the magnetic film. The rotation of the reflected light is known as the “Kerr Effect”. In phase change recording media, such as digital versatile discs (DVDs), information is read based on the difference in reflectivity due to the different absorption coefficients of an optical constant between an amorphous recorded domain and a crystalline non-recorded domain of the recording medium.

Recently, many diversified methods of recording information using micro marks (pits), as in a phase change method, and reproducing information from the recording medium regardless of the diffraction limit have been suggested. The most interested one among these methods is a recording method using a super-resolution near-field structure, which is disclosed in Applied Physics Letters, Vol. 73, No.15, October 1998, and Japanese Journal of Applied Physics, Vol. 39, Part I, No.2B, 2000, pp. 980-981. A super-resolution near-field structure utilizes local surface plasmon generated in a special mask layer to reproduce information. The super-resolution near-field structure is classified as an antimony (Sb) transmission type which has an antimony mask layer that becomes transparent by laser irradiation when reproducing information from the recording medium or as a silver oxide decomposition type which has a silver oxide (AgO_(x)) mask layer that decomposes into oxygen and silver, which acts as a scattering source inducing local plasmon.

FIG. 1 illustrates the structure of a recording medium using a conventional super-resolution near-field structure and the recording principle thereof. Such a structure as illustrated in FIG. 1 is referred to as “single-masked super-resolution near-field structure”.

As shown in FIG. 1, the recording medium includes a second dielectric layer 112-2 made of dielectric materials, for example, ZnS—SiO₂, a recording layer 115 made of, for example, GeSbTe, a protective layer 114 made of dielectric materials, for example, ZnS—SiO₂ or SiN, a mask layer 113 made of, for example, Sb or AgO_(x), a first dielectric layer 112-1 made of dielectric materials, for example, ZnS—SiO₂ or SiN, and a transparent polycarbonate layer 111, which are sequentially stacked upon one another. When the mask layer 113 is made of Sb, SiN is used for the protective layer 114 and for the first dielectric layer 112-1. When the mask layer 113 is made of AgO_(x), ZnS—SiO₂ is used for the protective layer 114 and for the first dielectric layer 112-1. The protective layer 114 prevents reaction between the recording layer 115 and the mask layer 113 and becomes a place where a near field acts when reproducing information. When reproducing the information, Sb of the mask layer 113 becomes transparent, and AgO_(x) of the mask layer 113 decomposes into oxygen and silver, which acts as a scattering source inducing local plasmon.

The recording medium is irradiated with a laser beam of about 10-15 mW emitted from a laser source 117 through a focusing lens 118 to heat the recording layer 115 above 600° C. so that a laser-irradiated domain of the recording layer 115 becomes amorphous and has a smaller absorption coefficient k regardless of the change of refractive index n of an optical constant (n,k). In an irradiated domain of the Sb or AgO_(x) mask layer 113, the crystalline structure of Sb changes or the quasi-reversible AgO_(x) decomposes, generating a probe as a near-field structure pointing at a region of the recording layer 115. As a result, it is possible to reproduce information recorded on the recording medium as micro marks which are smaller in size than a diffraction limit of the laser used. Therefore, it is possible to reproduce information recorded in a high-density recording medium using such a super-resolution near-field structure regardless of a diffraction limit of the laser used.

FIG. 2 illustrates the structure of a recording medium using another super-resolution near-field structure and the recording principle thereof. Such a structure as illustrated in FIG. 2 with two mask layers is referred to as “double-masked super-resolution near-field structure” and provides improved performance over a single-masked super-resolution near-field structure.

As shown in FIG. 2, the recording medium includes a second dielectric layer 122-2 made of dielectric materials, for example, ZnS—SiO₂, a second mask layer 123-2 made of, for example, Sb or AgO_(x), a second protective layer 124-2 made of dielectric materials, for example, ZnS—SiO₂ or SiN, a recording layer 125 made of, for example, GeSbTe, a first protective layer 124-1 made of dielectric materials, ZnS—SiO₂ or SiN, a first mask layer 123-1 made of, Sb or AgO_(x), a first dielectric layer 122-1 made of dielectric materials, for example, ZnS—SiO₂ or SiN, and a transparent polycarbonate layer 121, which are sequentially stacked upon one another. When the first and second mask layers 123-1 and 123-2 are made of Sb, SiN is used for the first and second protective layers 124-1 and 124-2 and the first and second dielectric layers 122-1 and 122-2. When the first and second mask layers 123-1 and 123-2 are made of AgO_(x), ZnS—SiO₂ is used for the first and second protective layers 124-1 and 124-2 and the first and second dielectric layers 122-1 and 122-2. The second mask layer 123-2 generates surface plasmon at a side of the recording medium opposite to the laser irradiation side. The first and second protective layers 124-1 and 124-2 prevent reaction between the recording layer 125 and the respective first and second mask layers 123-1 and 123-2. Particularly, the first protective layer 124-1 acts as a near field when reproducing information. When reproducing information, Sb of the first and second mask layers 123-1 and 123-2 becomes transparent, and AgO_(x) of the first and second mask layers 123-1 and 123-2 decomposes into oxygen and silver, which acts as a scattering source inducing local plasmon.

The recording medium is irradiated with a laser beam of about 10-15 mW emitted from a laser source 117 through a focusing lens 118 to heat the recording layer 125 above 600° C. so that a laser-irradiated domain of the recording layer 125 becomes amorphous and has a smaller absorption coefficient k, regardless of the change of refractive index n of an optical constant (n,k). In an irradiated domain of the first and second mask layers 123-1 and 123-2, which are made of Sb or AgO_(x), the crystalline structure of Sb changes or the quasi-reversible AgO_(x) decomposes, generating a probe as a near-field structure pointing at a region of the recording layer 125. As a result, it is possible to reproduce information recorded on the recording medium as micro marks which are smaller in size than a diffraction limit of the laser used. Therefore, it is possible to reproduce information recorded in a high-density recording medium using a super-resolution near-field structure regardless of a diffraction limit of the laser used.

However, in recording media having such a super-resolution near-field structure, since the mask layer and recording layer have similar transition temperatures, ensuring thermal stability to both the mask layer and the recording layer during information reproduction is important. Possible solutions to this problem include dropping the transition temperature of the mask layer and raising the transition temperature of the recording layer. However, it is not easy to induce a larger difference in transition temperature between the mask layer and the recording layer due to the nature of the materials forming the two layers.

SUMMARY OF THE INVENTION

According to an aspect of the present invention there is provided a simple-structured recording medium without a mask layer, the recording medium having a high melting point recording layer, an information recording method thereof, and an apparatus and method for reproducing information from the recording medium.

In accordance with another aspect of the present invention, there is provided a recording medium comprising a high melting point recording layer between first and second dielectric layers.

In accordance with another aspect of the present invention, there is provided a method of recording information on a recording medium having a high melting point recording layer between first and second dielectric layers, the method including irradiating a laser beam onto the recording medium to induce reaction and diffusion in the high melting point recording layer and the first and second dielectric layers.

In accordance with another aspect of the present invention, there is provided an apparatus of reproducing information from a recording medium having a high melting point recording layer between first and second dielectric layers, the apparatus generating plasmon using crystalline particles of the high melting point recording layer and the first and second dielectric layers as a scattering source to reproduce information recorded in the recording layer using a super-resolution near-field structure regardless of the diffraction limit of the laser used.

In accordance with another aspect of the present invention, there is provided a method of reproducing information from a recording medium having a high melting point recording layer between first and second dielectric layers, the method including generating plasmon using crystalline particles of the high melting point recording layer and the first and second dielectric layers as a scattering source to reproduce information recorded in the recording layer using a super-resolution near-field structure regardless of the diffraction limit of the laser used.

According to another aspect of the above-described recording medium, information recording method, and information reproducing apparatus and method, the high melting point recording layer may be formed of tungsten (W), tantalum (Ta), a tungsten compound (W-x), or a tantalum compound (Ta-x). An additional reflective layer may be formed underneath the second dielectric layer, for example, using silver (Ag) or aluminum (Al).

Additional aspects and/or advantages of the invention will be set forth in part in the description which follows and, in part, will be obvious from the description, or may be learned by practice of the invention.

BRIEF DESCRIPTION OF THE DRAWINGS

These and/or other aspects and advantages of the invention will become apparent and more readily appreciated from the following description of the embodiments, taken in conjunction with the accompanying drawings of which:

FIG. 1 illustrates the structure of a conventional recording medium using a super-resolution near-field structure and a recording principle thereof;

FIG. 2 illustrates the structure of another conventional recording medium using super-resolution near-field structure and the recording principle thereof;

FIGS. 3A and 3B illustrate a recording medium according to an embodiment of the present invention and the recording principle thereof, and in particular, FIG. 3B is an enlarged view of a recorded domain of FIG. 3A;

FIGS. 4A and 4B illustrate a recording medium according to another embodiment of the present invention and the recording principle thereof, and in particular, FIG. 4B is an enlarged view of a recorded domain of FIG. 4A; and

FIG. 5 is a comparative graph of a carrier to noise ratio (CNR) versus mark length for the recording media according to an aspect of the present invention and the conventional recording media.

DETAILED DESCRIPTION OF THE EMBODIMENTS

Reference will now be made in detail to the embodiments of the present invention, examples of which are illustrated in the accompanying drawings, wherein like reference numerals refer to the like elements throughout. The embodiments are described below to explain the present invention by referring to the figures.

A recording medium according to an embodiment of the present invention and the recording principle are illustrated in FIGS. 3A and 3B. In particular, FIG. 3B is an enlarged view of a recorded domain of FIG. 3A.

Referring to FIG. 3A, a recording medium according to an embodiment of the present invention includes a second dielectric layer 132-2 made of dielectric materials, for example, ZnS—SiO₂, a high melting point recording layer 135 made of, for example, tungsten (W), tantalum (Ta), a tungsten compound (W-x), or a tantalum compound (Ta-x), a first dielectric layer 132-1 made of dielectric materials, for example, ZnS—SiO₂, and a transparent polycarbonate layer 131, which are sequentially stacked upon one another.

The recording medium is irradiated with a laser beam of about 11 mW and 405 nm wavelength emitted from a high-power laser source 117 through a focusing lens 118 to heat the recording layer 135 equal to or above 600° C. to induce reaction and diffusion in a laser-irradiated domain. W, Ta, W-x, or Ta-x in the recording layer 135 diffuse into the first and second dielectric layers 132-1 and 132-2, interact with ZnS—SiO₂ composing the two dielectric layers, and are crystallized.

FIG. 3B illustrates a physical change in a laser-irradiated domain of the recording layer 135. As shown in FIG. 3B, the recording layer 135 has swollen at the laser-irradiated domain. A swollen portion of the recording layer 135 in the direction of the first dielectric layer 132-1 contributes to generating a near field when reproducing information. In addition, the crystalline particles of the recording layer 135 and the first dielectric layer 132-1 formed by the reaction and diffusion by laser irradiation act as a scattering source generating surface plasmon when reproducing information. As a result, it is possible to reproduce information recorded on the recording medium as micro marks which are smaller in size than a diffraction limit of the laser used. Therefore, it is possible to reproduce information recorded in a high-density recording medium using such a super-resolution near-field structure regardless of a diffraction limit of the laser used.

FIGS. 4A and 4B illustrate the structure of a recording medium according to another embodiment of the present invention and the recording principle thereof, and in particular, FIG. 4B is an enlarged view of a recorded domain of FIG. 4A.

Referring to FIG. 4A, a recording medium according to another embodiment of the present invention includes a reflective layer 146 made of, for example, silver (Ag) or aluminum (Al), a second dielectric layer 142-2 made of dielectric materials, for example, ZnS—SiO₂, a high melting point recording layer 145 made of, for example, tungsten (W), tantalum (Ta), a tungsten compound (W-x), or a tantalum compound (Ta-x), a first dielectric layer 142-1 made of dielectric materials, for example, ZnS—SiO₂, and a transparent polycarbonate layer 141, which are sequentially stacked upon one another.

The recording medium is irradiated with a laser beam of about 11 mW and 405 nm wavelength emitted from the high-power laser source 117 through the focusing lens 118 to heat the recording layer 145 equal to or above 600° C. to induce reaction and diffusion in a laser-irradiated domain. W, Ta, W-x, or Ta-x in the recording layer 145 diffuse into the first and second dielectric layers 142-1 and 142-2, interact with ZnS—SiO₂ composing the two dielectric layers, and are crystallized. The reflective layer 146, which is made of Ag or Al, induces reaction and diffusion in the side of the recording layer 145 opposite to the laser irradiation side and the second dielectric layer 142-2, to a similar degree as the reflective layer induces reaction and diffusion in the side of the recording layer 145 and the first dielectric layer 142-1 onto which the laser beam is directly irradiated, enhancing the effect of the reaction and diffusion in the directly laser-irradiated side.

FIG. 4B illustrates a physical change in the laser-irradiated domain of the recording layer 145. As shown in FIG. 4B, the recording layer 145 is swollen at the laser-irradiated domain. A swollen portion of the recording layer 145 in the direction of the first dielectric layer 142-1 contributes to generating a near field when reproducing information. In addition, the crystalline particles of the recording layer 145, the first dielectric layer 142-1 and the second dielectric layer 142-2 formed by the reaction and diffusion by laser irradiation act as a scattering source generating surface plasmon when reproducing information. As a result, it is possible to reproduce information recorded on the recording medium as micro marks which are smaller in size than a diffraction limit of the laser used. Therefore, it is possible to reproduce information recorded in a high-density recording medium using such a super-resolution near-field structure regardless of a diffraction limit of the laser used.

FIG. 5 is a comparative graph of a carrier to signal ratio (CNR) versus mark length for the recording media according to an embodiment of the present invention and conventional recording media. Recording was performed on the recording media according to an embodiment of the present invention by inducing reaction and diffusion in the recording layer made of tungsten by irradiating a 405-nm laser at a power of 11 mW, through a focusing lens having a numerical aperture of 0.65. Reproduction was performed using a 405-nm laser at a power of 4 mW and a focusing lens having a numerical aperture of 0.65. For the conventional super-resolution near-field recording media of FIGS. 1 and 2 and a general phase change-recording medium, recording and reproduction were performed using the same laser under the same conditions as for the recording media according to the embodiment of the present invention.

As illustrated in FIG. 5, the CNR with respect to varying mark lengths is greatest for the super-resolution near-field recording medium of FIG. 4 and decreases in FIG. 3, the conventional super-resolution near-field recording medium of FIG. 2, the conventional super-resolution near-field recording medium of FIG. 1, and a general phase change recording medium. This indicates that high-density recording can be achieved with the super-resolution near-field structure of FIG. 4 according to the present invention, at a high CNR of about 45 dB for a mark length of 170 nm.

As described above, a recording medium with a high melting point recording layer and without a mask layer according to an aspect of the present invention is suitable for high-density recording and reproduction, using the recording and reproducing methods and apparatus according to the present invention, without causing the thermal stability related problems arising when reproducing information from conventional super-resolution near-field recording media. The recording medium according to an aspect of the present invention is low in cost due to its simple structure.

Although a few embodiments of the present invention have been shown and described, it would be appreciated by those skilled in the art that changes may be made in these embodiments without departing from the principles and spirit of the invention, the scope of which is defined in the claims and their equivalents. 

1. A recording medium comprising a high melting point recording layer between first and second dielectric layers.
 2. The recording medium of claim 1, wherein the high melting point recording layer is formed of tungsten.
 3. The recording medium of claim 1, wherein the high melting point recording layer is formed of tantalum.
 4. The recording medium of claim 1, wherein the high melting point recording layer is formed of a tungsten compound.
 5. The recording medium of claim 1, wherein the high melting point recording layer is formed of a tantalum compound.
 6. The recording medium of claim 1, further comprising a reflective layer on the second dielectric layer.
 7. A method of recording and/or reproducing information on/from a recording medium having a high melting point recording layer between first and second dielectric layers, the method comprising irradiating a laser beam onto the recording medium to induce reaction and diffusion in the high melting point recording layer and the first and second dielectric layers.
 8. The method of claim 7, wherein the high melting point recording layer is formed of tungsten.
 9. The method of claim 7, wherein the high melting point recording layer is formed of tantalum.
 10. The method of claim 7, wherein the high melting point recording layer is formed of a tungsten compound.
 11. The method of claim 7, wherein the high melting point recording layer is formed of a tantalum compound.
 12. The method of claim 7, wherein the recording medium further comprises a reflective layer on the second dielectric layer.
 13. An apparatus reproducing information from a recording medium having a high melting point recording layer between first and second dielectric layers, the apparatus generating plasmon using crystalline particles of the high melting point recording layer and the first and second dielectric layers as a scattering source to reproduce information recorded in the recording layer using a super-resolution near-field structure regardless of a diffraction limit of a laser.
 14. The apparatus of claim 13, wherein the high melting point recording layer is formed of tungsten.
 15. The apparatus of claim 13, wherein the high melting point recording layer is formed of tantalum.
 16. The apparatus of claim 13, wherein the high melting point recording layer is formed of a tungsten compound.
 17. The apparatus of claim 7, wherein the high melting point recording layer is formed of a tantalum compound.
 18. The apparatus of claim 13, wherein the recording medium further comprises a reflective layer on the second dielectric layer.
 19. A method of reproducing information from a recording medium having a high melting point recording layer between first and second dielectric layers, the method comprising generating plasmon using crystalline particles of the high melting point recording layer and the first and second dielectric layers as a scattering source to reproduce information recorded in the recording layer using a super-resolution near-field structure regardless of a diffraction limit of a laser.
 20. The method of claim 19, wherein the high melting point recording layer is formed of tungsten.
 21. The method of claim 19, wherein the high melting point recording layer is formed of tantalum.
 22. The method of claim 19, wherein the high melting point recording layer is formed of a tungsten compound.
 23. The method of claim 19, wherein the high melting point recording layer is formed of a tantalum compound.
 24. The method of claim 19, wherein the recording medium further comprises a reflective layer on the second dielectric layer.
 25. A high-density recording medium comprising: a polycarbonate layer; a first dielectric layer; a recording layer; and a second dielectric layer, wherein crystalline particles of the recording layer and the first and second dielectric layers generate surface plasmon when reproducing information of the high-density recording medium.
 26. The high-density recording medium of claim 25, wherein the recording layer is a high melting point recording layer.
 27. The high-density recording medium of claim 25, wherein the recording medium is irradiated with a laser beam of approximately 11 mW and 405 nm wavelength, heating the recording layer to approximately 600° C.
 28. The high-density recording medium of claim 25, wherein the recording layer comprises tungsten, tantalum, a tungsten compound, and/or a tantalum compound.
 29. The high-density recording medium of claim 25, further comprising a reflective layer formed on the second dielectric layer.
 30. The high-density recording medium of claim 29, wherein the reflective layer comprises aluminum and/or silver.
 31. A method of recording and/or reproducing information from and/or on a recording medium having a recording layer formed between first and second dielectric layers, the method comprising: irradiating the recording medium with a laser beam; heating the recording layer inducing a reaction and diffusion in a laser-irradiated domain; forming crystalline particles in the recording layer and the first and second dielectric layers; and recording and/or reproducing information on the information medium in the form of marks smaller in size than a diffraction limit of the laser beam.
 32. The method of claim 31, wherein the laser beam irradiating the recording medium is of approximately 11 mW and 405 nm wavelength.
 33. The method of claim 32, wherein the recording layer is heated to approximately 600° C.
 34. The method of claim 31, wherein the recording and/or reproducing of the information on the recording medium is achieved with a carrier to signal ratio (CNR) of approximately 45 dB for a mark length of 170 nm. 